The experiments to produce the vaterite type calcium carbonate were conducted for using the waste oyster shell as the recycling resources. Firstly, the oyster shell were calcinated at 800 degrees C for 24 h. Calcinated oyster shell were reacted with the nitric acid solution, and were diluted to 0.1 M Ca(NO3)(2) solution. This solution was mixed with 0.1 M Na2CO3 contained 0.1 mol lysine/1 mol CaO at 20 degrees C and 600 rpm mixing condition for 1 h. The reaction products were identified to vaterite type calcium carbonate (84.5% vaterite, 15.5% calcite) by XRD and SEM analysis. Mean particle diameter was 6.87 mu m, and the lysine content in calcium carbonate was analyzed to 0.1%.