Poly(1,4-bis((E)-2-(3-dodecylthiophen-2-yl)vinyl)benzene) for Solution Processable Organic Thin Film Transistor

초록

New semiconducting polymer, poly[1,4-bis((E)-2-(5-bromo-3-dodecylthiophen-2-yl)vinyl)benzene], was designed, synthesized and characterized. The structure of polymer was confirmed by H-1-NMR., IR and elemental analysis. The polymer was soluble in specific organic solvent. The weight-average molecular weights (MW) of polymer was found to be 11,000 with polydispersity of 1.82. UV-Visible absorption spectrum showed the maximum absorption at 428 nm (in solution) and 438 nm (in film). The highest occupied molecular orbital (HOMO) energy of the polymer is -5.36 eV by measuring cyclic voltammetry (CV). A solution-processed polymer thin film transistor device shows a mobility of 8.59 x 10(-4) cm(2) V-1 s(-1), an on/off current ratio of 2.0 x 10(4).