Parametric estimation analysis of compressive stress effects on piezoelectric properties of PZT ceramic

초록

In this study, the frequency and capacitance of piezoelectric materials due to compressive stress were analyzed, and the overall material properties (compliance matrix, piezoelectric charge constant and dielectric constant) of piezoelectric ceramics were optimized using parametric estimation methods. The piezoelectric ceramic used for optimization was KICET-PZT8, and the compressive stress was applied from a stress-free condition up to 50 MPa. As a result, with increasing compressive stress, the values of (Formula presented.), (Formula presented.) and (Formula presented.) tended to increase, while (Formula presented.) and (Formula presented.) increased and then decreased at 20 MPa or higher. (Formula presented.) and (Formula presented.) showed the maximum values at 40 MPa of compressive stress, with the values reaching 147 pC/N and 375 pC/N, respectively. These values were analyzed to have increased by 117% and 115%, respectively, compared to the stress-free condition. Additionally, the dielectric constant ((Formula presented.)) was found to increase linearly with the applied compressive stress. The understanding of the changes in piezoelectric properties under various compressive stresses derived from this study is expected to be applicable in various ways for the design and application of piezoelectric devices using compressive stresses, including BLT. © 2023 The Author(s). Published by Informa UK Limited, trading as Taylor & Francis Group on behalf of The Korean Ceramic Society and The Ceramic Society of Japan.

키워드