Statistical description of the effect of Zr addition on the behavior of microcracks in Cu-6Ni-2Mn-2Sn-2Al Alloy

Abstract

As possible substitutes for high-strength Cu-Be alloys, Cu-6Ni-2Mn-2Sn-2Al alloys have been developed. To clarify the physical background of the effect of trace Zr on the fatigue strength of such alloys, the initiation and propagation behavior of a major crack that led to the fracture of the tested specimens was monitored. When the stress amplitude was less than sigma(a) = 350 MPa, the fatigue life of the alloys with Zr was about 2-2.5 times larger than that of the alloy without Zr. When sigma(a) > 350 MPa, the effect of Zr addition on the fatigue life dramatically decreases as the stress amplitude increases. The increased fatigue life due to Zr addition resulted from an enhancement of the crack initiation life and microcrack growth life. The enhanced crack initiation life was mainly attributed to the strengthening of grain boundaries due to the precipitation of SnZr compounds. A statistical analysis of the behavior of multiple cracks was made to quantitatively evaluate the scatter in fatigue behavior. The statistical analysis supported the conclusions obtained from the behavior of a major crack.